Metal-ceramic composite substrates, producing methods thereof and brazing materials for use in such method

ABSTRACT

In the present invention, a metal-ceramic composite substitute is produced by joining a metal plate to a ceramic substrate by using a brazing material in a paste form prepared by adding 10-14 parts by weight of a vehicle to 100 parts by weight of a powder of which the solid centent comprises 90.0˜99.5% of an Ag powder, 0˜9.5% of a Cu powder and 0.5˜4.0% of an active metal powder, and 0.0˜0.9% of a titanium oxide powder if necessary.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to metal-ceramic composite substrates, and producing methods thereof. The invention also relates to brazing materials that can effctively be used in joining metals to ceramic substrates.

2. Description of the Prior Art

Several methods are known in the art of joining metal such as copper plates to ceramic substrates such as aluminum nitride (AlN) and two typical examples are the active metal brazing process described in Japanese Patent Laid-Open No.166165/1985 entitled “A method of Joining Nitride-Base Ceramics to Metals” and the process in which a copper plate is directly joined to a modified surface of an aluminum nitride substrate (as typically described in Japanese Patent Laid-Open No. 163093/1981).

The active metal brazing process provides a higher strength of joint than the direct joining process and the resulting joint has the desired charactristics such as high durability to repeated heat cycles. Hence, the active metal brazing process currently finds extensive use in the joining of copper plates to non-oxide-base ceramic substrates, say, nitride ceramic substrates.

Two brazing materials are commercially used in the practice of the active metal brazing process; one of them is composed of Ag, Cu and an active metal selected from among Ti, Zr and Hf (as described in Japanese Patent Laid-Open No.166165/1985) and the other is an active metal paste material composed of Ag, Cu and titanium hydride (as described in Japanese patent Laid-Open No.101153/1991).

Circuit substrates produced by joining copper plates to both sides of an aliminum nitride substrate with the aid of these brazing materials have already been commercialized.

In many brazing materials, an active metal is added to a structure comprising 72% of Ag and 28% of Cu, and accordingly the joining process is carried out at a temperature higher than the eutectic point of 780° C., preferably, at a temperature of around 850° C.

However, most recent circuit substrates are required to perform on larger electrical power and to meet this requirement, it has been desired to develop circuit substrates that are not only provided with good heat dissipating and electrical insulating properties but which also exhibit higher strength and thermal impact resistance.

SUMMARY OF THE INVENTION

An object, therefore, of the invention is to provide a brazing material that is suitable for use in the manufacture of power module composite substrates having no non-contact portions and which is capable of improving their charactristics than the conventional brazing materials.

Another object of the invention is to provide a process for producing metal-ceramic composite substrates using the brazing material.

The present inventors conducted intensive studies in order to attain the stated objects and found that joining processes could be carried out at a temperature of 780° C.˜870° C. lower than the eutectic point of 875° C. by using active metal brazing materials added with 90% of Ag and 9.5% of Cu or 0.5% of an active metal (TiO), and that the jointed composite substrates had no non-contact portions.

The present invention has been accomplished on the basis of this finding.

According to a first aspect of the invention, there is provided a metal-ceramic composite substrate produced by joining a metal plate to a ceramic substrate by using a brazing material of which the solid content comprises 90.0˜99.5% of Ag, 0˜9.5% of Cu, 0.5˜4.0% of an active metal on a weight basis.

Said ceramic substrate is at least one kind of ceramic substrate selected from a group consisting of Al₂O₃, AlN and Si₃N₄O.

Said active metal is at least one active metal selected from a group consisting of Ti, Zr and Hf.

According to a second aspect of the invention, there is provided a process for producing a metal-ceramic composite substrate by joining a metal plate to a ceramic substrate, which comprises the steps of:

adding 10-14 parts by weight of a vehicle to 100 parts by weight of a powder of which the solid content comprises 90.0˜99.5% of an Ag powder, 0˜9.5% of a Cu powder and 0.5˜4.0% of an active metal powder on a weight basis;

blending the respective ingredients to form a brazing material in a paste form;

applying the brazing material to the ceramic substrate;

superposing a metal plate on the applied brazing material and heating the assembly at a temperature not higher than the melting point of the brazing material to form a joint of the metal plate and the ceramic substrate; and

applying an etching resist on the metal plate of the joint to form a circuit pattern and etching the metal plate to form a metalized circuit.

Said heating temperature of the assembly is in the range of 780° C. to 870° C. which is not higher than the temperarure of the melting point of the brazing material.

According to a third aspect of the invention, there is provided a brazing material for use in joining a metal plate to a ceramic substrate, which is in a paste form prepared by blending 10-14 parts by weight of a vehicle with 100 parts by weight of a powder of which the solid content comprises 90.0˜99.5% of an Ag powder, 0˜9.5% of a Cu powder and 0.5˜4.0% of an active metal powder on a weight basis.

According to a fourth aspect of the invention, there is provided a brazing material for use in joining a metal plate to a ceramic substrate, which is in a paste form prepared by blending 10-14 parts by weight of a vehicle with 100 parts by weight of a powder of which solid content comprises 90.0˜99.5% of an Ag powder, 0˜9.5% of a Cu powder, 0.5˜4.0% of an active metal powder and 0.0˜0.9% of a titanium oxide powder on a weight basis.

The brazing material to be used in the invention has an Ag content of 90.0˜99.5 wt %. If the Ag content is less than 90 wt % unsuitable composite substrates having non-contact portions will be produced.

The Cu content of the brazing material is less than 9.5 wt %. The reason why the Cu content is smaller than that of the conventional Ag—Cu brazing material is that when the assembly is heated the Ag component and the contact surface of the copper plate are reacted to create the eutectic crystalization.

The active metal that can be used in the invention is at least one element of group IVa of the periodic table as exemplified by Ti, Zr or Hf.

These active metals may be added either in an elemental form or as a hydride and the preferred amount of their addition ranges from 0.5 to 4.0 wt %.

Below 0.5 wt %, a nitride layer will form in an insufficient amount to provide the necessary adhesive strength; beyond 4.0 wt %, the adhesive strength is increased, but, on the other hand, cracking is prone to occur after joining a metal plate to a cearmic substrate.

Titanium oxide is added as TiO or TiO₂ In an amount ranging from 0.0 to 0.9 wt %. The titanium oxide may be amorphous or crystalline.

The present inventors confirmed by experimets that adding these amount of titanium oxide to a brazing material of the composition described above contributed to improvements in various characteristics of the resulting composite substrates such as resistance to repeated heat cycles, flexural strength, deflection and resistance to the passage through a furnace. A probable reason for these contributions would be that the TiO₂ or TiO added to the brazing material is dispersed uniformly to reduce the concentration of stresses.

An alloy having the above-defined composition may be directly used as the brazing material of the invention. Alternatively, a powder comprising the particles of the respective ingredients may be mixed with an organic solvent to form a paste of the brazing material. If a metal member is to be simply joined to a ceramic member, the brazing alloy material in the form of a plate or a foil may be used. If an electronic circuit is to be formed on a ceramic substrate, a paste of the brazing material is preferably used.

In order to prepare the paste of brazing material, 55-75 parts by volume of an organic solvent such as terpineol, toluene, methyl cellosolve or ethyl cellosolve may be mixed with 25-45 parts by volume of an organic binder such as PMMA, methyl cellulose or ethyl cellulose to form a vehicle, which is then added in an amount of 10-14 parts by weight to 100 parts by weight of the powder comprising the particles of the respective ingredients for the brazing material.

If less than 10 parts by weight of the vehicle is used, the resulting paste is so viscous that blurred prints will tend to occur. If more than 14 parts by weight of the vehicle is used, the resulting paste is so low in viscosity that print washout will readily occur.

The present invention is characterized in that the assembly is heated in the furnace at a temperature lower than the eutectic melting point of the brazing material, preferably at 780° C.-870° C. according to the composition of the brazing material for the reasons mentioned below.

In case that the conventional brazing material formed of 72% of Ag and 28% of Cu added with an active metal Ti is used, the joining is intiated at a temperature higher than the eutectic melting point of Ag—Cu, that is, of 780° C. . Accordingly, in practice, the joining is carried out at a temperature of around 850° C. In the present invention, the amount of Ag is more than 90 wt %. If Ag is 90 wt %, Cu is 9.5 wt % and Ti is 0.5 wt %, the eutectic melting point should be a temperature more than 875° C. in consideration of the phase diagram of silver-copper, so that the joining have to be carried out at a temperature of around 90° C. in order to obtain a perfect joint in the conventional process.

If the brazing material of the present invention only is heated at a temperature lower than said eutectic melting point (875° C.), it may not be molten but merely sintered. However, in case of using a copper plate as a substrate for the power module as in the present invention, said brazing material and the copper plate are brought into contact with each other, so that when the assembly is heated Ag in the brazing material and Cu in the copper plate are reacted eutecticlly gradually from said contact portion in the micron order, Ag is diffused gradually into the copper plate started from said reaction and the eutectic structure is formed on the whole contact surface.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The following examples are provided for the purpose of further illustrating the present invention but are in no way to be taken as limiting.

EXAMPLE 1

An AlN substrate measuring 53×29×0.635 mm was provided as a ceramic substrate. 100 parts by weight of a powder of which the solid content was shown in a Table 1(Samples 1-8) were mixed with 12.4 parts by weight of a vehicle to prepare a paste of brazing material. After applying the paste to the whole surface of the AlN substrate, two copper plates having thicknesses of 0.3 mm and 0.15 mm, respectively, were superposed on the repective sides and the assembly was fired at temperatures shown in the Table 1 to produce a joint.

TABLE 1 NUMBER OF RATE OF JOINT HAVING JOINT HAVING BRAZING MATERIAL wt % FIRING NUMBER OF NON-CONTACT NON-CONTACT SAMPLE Ag Cu Ti TEMPERATURE TEST PIECE SURFACE SURFACE NO. 1 90.0 9.5 0.5 800° C. 100 1 1 830 100 0 0 860 100 0 0 NO. 2 90.0 8.0 2.0 800 100 1 1 830 100 0 0 860 100 0 0 NO. 3 90.0 6.0 4.0 800 100 0 0 830 100 0 0 860 100 0 0 NO. 4 99.5 0 0.5 800 100 0 0 830 100 0 0 860 100 0 0 NO. 5 98.0 0 2.0 800 100 0 0 830 100 0 0 860 100 0 0 NO. 6 96.0 0 4.0 800 100 0 0 830 100 0 0 860 100 0 0 NO. 7 90.0 9.5 Ti/TiO₂ 800 100 0 0 0.25 830 100 0 0 0.25 860 100 0 0 NO. 8 99.5 0 0.25 800 100 0 0 0.25 830 100 0 0 860 100 0 0

The 100 pieces of each of the samples were tested at many firing temperatures for detecting the non-contact portions.

The results show that the samples having non-contact portion are few.

COMPARATIVE EXAMPLE 1

An AIN substrate of the same dimensions as described in Example 1 was provided as a ceramic substrate.

100 parts by weight of a powder of which the solids content was shown in a Table 2(Comparative Samples 1-6) were mixed with 12.4 parts by weight of a vehicle to prepare a paste of brazing material. After applying the paste to the whole surface of the AlN substrate, two copper plates having thicknesses of 0.3 mm and 0.15 mm, respectively, were superposed on the respective sides and the assembly was fired at temperatures shown in the Table 2 to produce a joint.

TABLE 2 NUMBER OF RATE OF JOINT HAVING JOINT HAVING COMPARATIVE BRAZING MATERIAL wt % FIRING TEST PIECE NON-CONTACT NON-CONTACT SAMPLE Ag Cu Ti TEMPERATURE NUMBER OF SURFACE SURFACE NO. 1 72.0 27.5 0.5 800° C. 100 81 81% 830 100 43 43 860 100 13 13 NO. 2 72.0 26.0 2.0 800 100 75 75 830 100 11 11 860 100 6  6 NO. 3 72.0 24.0 4.0 800 100 68 68 830 100 10 10 860 100 5  5 NO. 4 80.0 19.5 0.5 800 100 31 31 830 100 13 13 860 100 5  5 NO. 5 80.0 18.0 2.0 800 100 25 25 830 100 8  8 860 100 4  4 NO. 6 80.0 16.0 4.0 800 100 20 20 830 100 6  6 860 100 3  3

The 100 pieces of each of the samples were tested at many firing temperatures for detecting the non-contact portions as like as the Example 1.

The results show that the many samples having non-contact portion are produced according to the decrease of the Ag density and the firing temperature as shown in the Table 2.

As described on the foregoing pages, the metal-ceramics composite substrates produced by using the brazing material of the present invention are sufficiently improved in the reduction of the non-contact portions, and can be manufactured efficiently with low cost.

While the invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the sprit and scope of the ivention as defined by the appended claims. 

What is claimed is:
 1. A metal-ceramic composite substrate comprises a metal plate, a ceramic substrate, and a brazing material by which said ceramic substrate is joined to the metal plate at a temperature not higher than the temperature of the melting point of the brazing material, said brazing material being in a paste form comprising a powder of which the solid content comprises 90.0˜99.5% of Ag, greater than 0% and less than 9.5% of Cu, 0.5%˜4.0% active metal on a weight basis and 10˜14 parts by weight of a vehicle corresponding to 100 parts by weight of said powder.
 2. The metal-ceramic composite substrate as claimed in claim 1, wherein the ceramic substrate is at least one kind of ceramic substrate selected from a group consisting of Al₂O₃, AlN and Si₃N₄.
 3. The metal-ceramic composite substrate as claimed in claim 1, wherein the active metal is at least one active metal selected from a group consisting of Ti, Zr and Hf. 